BOPP Hologram Film
The laser surface is smooth and clean
Excellent laser molding effect
Clear molding
Metallised after laser
Product Advantages
Category
|
Product Category |
Product Type |
|---|---|
| laser film | PAL |
| Laser matte film | MPAL |
| Chemical film | CPAL |
| Laser wire-draw film | WPAL |
| Laser pearlised film | PEAPAL |
Note: The above BOPP laser base film can be customized for clients according to specific application demand.
Performance
| BOPP Laser Base Film PAL | |||||
|---|---|---|---|---|---|
| Property | Unit | Typical Values | Reference | Method | |
| Thickness | μm | 22.0 | +/- 3% | GB/T 6672 | |
| Density | g/cm3 | 0.905 | +/- 2% | GB/T 1033.1 | |
| Weight | g/m2 | 19.9 | +/- 2% | GB/T 6672 | |
| Yield | m2/kg | 50.3 | +/- 2% | GB/T 6672 | |
| Tensile strength | MD | N/mm2 | 134 | ≥120 | GB/T 1040.3 |
| TD | N/mm2 | 287 | ≥200 | GB/T 1040.3 | |
| Thermal shrinkage (105°C 2mins) |
MD | % | 3.50 | ≤4.0 | GB/T 10003 |
| TD | % | 0.61 | ≤1.0 | GB/T 10003 | |
| Elongation at break | MD | % | 149 | ≤180 | GB/T 1040.3 |
| TD | % | 55 | ≤80 | GB/T 1040.3 | |
| Coefficient of Friction | Wound inside | - | 0.41 | ≤0.80 | GB/T 10006 |
| Wound outside | - | 0.74 | ≤1.0 | GB/T 10006 | |
| Haze | % | 1.06 | ≤2.0 | GB/T 2410 | |
| Gloss（45°） | % | 91.5 | ≥85.0 | GB/T 8807 | |
| Sealing strength（125°） | n/15mm | 3.69 | ≥2.5 | ZBYZB8004 | |
The information on Weifu products and their applications provided in this data sheet is based on testing of representative material. The information does not constitute a warranty or guarantee, either expressly or implied, of any specific product attribute or the suitability of products for specific applications. For particular technical requirements or specifications, please contact Weifu.
Avoid mechanical impact, exposure to sunlight and rain during transportation. BOPP laser film should be stored below 50% RH, temperature below 30°C, away from direct sunlight. Suitable for use for up to 6 months.
Application
BOPP laser base film can be metallised after laser, with excellent metal stereoscopic sense.It is suitable for all kinds of laser molding machines, widely used in trademarks and anti-counterfeiting LOGO.