BOPP White Film
Realistic printing color
Paper-like appearance
Smooth film surface
Delicate and soft films appearance
Product Advantages
Category
|
Product Category |
Product Type |
|---|---|
|
White film |
IML |
Performance
| BOPP White film | |||||
|---|---|---|---|---|---|
| Property | Unit | Typical Values | Reference | Method | |
| Thickness | μm | 28.0 | +/- 2μ m | GB/T 6672 | |
| Density | g/cm3 | 0.930 | +/- 2% | GB/T 1033.1 | |
| Weight | g/m2 | 26.1 | +/- 2% | GB/T 6672 | |
| Yield | m2/kg | 38.3 | +/- 2% | GB/T 6672 | |
| Tensile strength | MD | N/mm2 | 142 | ≥120 | GB/T 1040.3 |
| TD | N/mm2 | 312 | ≥220 | GB/T 1040.3 | |
|
Thermal shrinkage |
MD | % | 3.26 | ≤4.0 | GB/T 10003 |
| TD | % | 0.16 | ≤1.0 | GB/T 10003 | |
| Elongation at break | MD | % | 181 | ≤240 | GB/T 1040.3 |
| TD | % | 54 | ≤65 | GB/T 1040.3 | |
| Coefficient of Friction | Corona treated side | - | 0.72 | ≤0.60 | GB/T 10006 |
| Corona untreated side | - | 0.68 | ≤0.60 | GB/T 10006 | |
| Haze | % | 97.4 | ≤1.6 | GB/T 2410 | |
| Gloss（45°） | % | 49.0 | ≥90.0 | GB/T 8807 | |
| Impact resistance strength | J | 2.095 | ≥0.5 | - | |
| Wetting tension (One side) | mN/m | 38 | ≥38 | GB/T14216 | |
The information on Weifu products and their applications provided in this datasheet is based on testing of representative material and the results are believed to be reliable as at the date of publication advised below. The information does not constitute a warranty or guarantee, either expressly or implied, of any specific product attribute or the suitability of products for specific applications. For particular technical requirements or specifications, please contact Weifu.
Avoid mechanical impact, exposure to sunlight and rain during transportation. BOPP white film should be stored below 50% RH, temperature below 30°C, away from direct sunlight. Suitable for use for up to 6 months.
Application
It could be used for C=container labels with good recognition effect to replace paper labels. It is specially used for advanced labels with various functions. It can be laminated with other materials according to the functional requirements.