CPP Film

Low temperature heat sealable Low temperature heat sealable

Good flatness Good flatness

High transparency High transparency

Soft and low odour Soft and low odour

Product Advantages

Low temperature heat sealable

Good flatness

High transparency

Good slip properties

Soft and low odour

Suitable for inflated bags

Food Contact

Compliant with international food contact standards.

Product features


Product Category

Product Type

Lamination film


Increased toughness/freezer film


Tissue film

Coated film CPH/CPL
Protective film PFC
Degradable film LOD2
Aluminum-plastic base film BL1
Photo album card film LCNT

Anti-ageing film


Note: The above CPP film can be customized for clients according to specific application demand.


CPP Heat Sealable Film (L2)
Property Unit Reference Method
Thickness μm 20 25 30 40 50 60 GB/T 6672
Density g/cm3 0.89 0.89 0.89 0.89 0.89 0.89 GB/T 1033.1
Weight g/m2 17.8 22.3 26.7 35.6 44.5 53.4 GB/T 6672
Yield m2/kg 56.2 44.9 37.5 28.1 22.5 18.7 GB/T 6672
Tensile strength MD MPa ≥35 GB/T 1040.3
TD MPa ≥25 GB/T 1040.3
Elongation at break MD % ≥350 GB/T 1040.3
TD % ≥450 GB/T 1040.3
Wetting tension Corona treated side mN/m ≥36 GB/T 14216

Corona untreated side

mN/m <33 GB/T 14216
Coefficient of Friction Corona treated side - ≥0.45 GB/T 10006

Corona untreated side

- ≤0.15 GB/T 10006
Haze % ≤2.5 ≤3.0 ≤3.2 ≤3.5 ≤4.3 ≤5.2 GB/T 2410

Heat seal range(Note 1)

≤125 GB/T 27740


Note 1:


sealing strength




≥40um ≥12N


The information on Weifu products and their applications provided in this data sheet is based on testing of representative material. The information does not constitute a warranty or guarantee, either expressly or implied, of any specific product attribute or the suitability of products for specific applications. For particular technical requirements or specifications, please contact Weifu.


CPP film can be printed or laminated with BOPP or other materials. It is suitable for automatic packaging and bag making equipment for food and daily necessities packaging.