PE Metallised Film
Excellent temperature resistance
Accurate overprinting
Excellent puncture resistance
Excellent oxygen and water vapor transmission rate barrier properties
Product Advantages
Category
| Product catalogue | Product type |
|---|---|
| CPE metallised film | AlMCPE |
| BOPE metallised film | AlMBOPE |
Remark: The above PE metallised film can be customized for clients according to their specific application demand.
Performance
| BOPE metallised film(ALMBOPE) | |||||
|---|---|---|---|---|---|
| Property | Unit | Typical Values | Reference | Method | |
| Thickness | μm | 25 | +/-6% | GB/T 6672 | |
| Density | g/cm3 | 0.94 | +/- 2% | GB/T 1033.1 | |
| Weight | g/m2 | 23.5 | +/- 2% | GB/T 6672 | |
| Yield | m2/kg | 42.55 | +/- 2% | GB/T 6672 | |
| Tensile strength | MD | N/mm2 | 83 | ≥60 | GB/T 1040.3 |
| TD | N/mm2 | 160 | ≥150 | GB/T 1040.3 | |
| Thermal shrinkage (100°C 2mins) |
MD | % | 4.5 | ≤8.0 | GB/T 10003 |
| TD | % | 2.5 | ≤4.0 | GB/T 10003 | |
| Elongation at break | MD | % | 360 | ≤400 | GB/T 1040.3 |
| TD | % | 70 | ≤100 | GB/T 1040.3 | |
| Coefficient of Friction | Metallised side | - | 0.21 | ≤0.4 | GB/T 10006 |
| Non-metallised side | - | 0.18 | ≤0.4 | GB/T 10006 | |
| Optical density | N/15mm | 2.4 | ≥1.8 | ANSI/NAPMIT2.19 | |
| Metallised adhesion bonding strength | N/15mm | 2.0 | ≥1.5 | - | |
| Oxygen transmission rate | Cm3/m2·d·0.1Mpa | 113 | - | GB/T1038-2000 | |
| Water vapor transmission rate | g/m2.24h | 1.26 | - | ASTM F1249-2001 | |
| Wetting tension（one side） | mN/m | 37 | ≥35 | GB/T14216 | |
The information on Weifu products and their applications provided in this datasheet is based on testing of representative material and the results are believed to be reliable as at the date of publication advised below. The information does not constitute a warranty or guarantee, either expressly or implied, of any specific product attribute or the suitability of products for specific applications. For particular technical requirements or specifications, please contact Weifu.
Application
Used for printing, lamination and pouch making. Suitable for food packaging and daily chemical packaging.